Alumina Castable 35% Al2O3 P-CAST-A35
Alumina Castable 35% Al2O3 P-CAST-A35 is a conventional castable based on fireclay with Min. 22% Al2O3, suitable for service temperatures up to 1250 °C. It has a hydraulic bond and is installed by casting with vibration.
- Product family
- Castables & Ramming Mixes
- Last updated
Product overview & application
About Alumina Castable 35% Al2O3 P-CAST-A35
Alumina Castable 35% Al2O3 P-CAST-A35 is a conventional castable based on fireclay with Min. 22% Al2O3, suitable for service temperatures up to 1250 °C. It has a hydraulic bond and is installed by casting with vibration. Material type according to the datasheet: Dense refractory concrete; raw material basis: fireclay.
Conventional castables contain more calcium aluminate cement. They are easy to install, but need more water and have a higher porosity after firing than low cement grades, so they are not intended for direct contact with molten metal.
Technical properties
- Maximum service temperature: 1250 °C
- Al2O3: Min. 22%
- Bulk density: Approx. 2 g/cm³
- Grain size: 0 – 5 mm
- Cold crushing strength after drying at 110 °C: 250 – 450 kg/cm²
Installation, packaging and storage
Installation: casting with vibration. Water addition, drying and initial heat-up should follow the manufacturer's instructions to achieve the best properties. Packaging: 40 kg bags (dry mix, water is added on site). Shelf life: 6 months (dry, cool, frost-free place).
The values in the specification table are taken from the product datasheet. Contact the Pas Espadana technical team to select the right grade for your operating conditions.
Applications
- Linings of furnaces and thermal equipment up to 1250 °C
- General refractory linings and repairs
Information needed for review
- Service temperature and type of equipment
- Installation method and lining thickness
- Chemical and mechanical conditions (slag, alkalis, abrasion)
- Required quantity and delivery time
Technical specifications
| Maximum service temperature | 1250°C |
|---|---|
| Bulk density | Approx. 2g/cm³ |
| Grain size | 0 – 5mm |
| Cold crushing strength (110 °C) | 250 – 450kg/cm² |
| Al2O3 | Min. 22% |
| CaO | 8 – 10% |
| Installation | Casting with vibration |
Selection based on your conditions
Contact our technical team to review grades, supply and to receive a valid document.
Request product consultation